搜索结果: 1-5 共查到“材料力学 Ni3Al”相关记录5条 . 查询时间(0.065 秒)
Cast in situ composites of Ni3Al / MeC type
Composite in situ Intermetallic phase SHSB Process Exothermic reaction Carbides of TiC WC ZrC NbC TaC
2011/3/30
In this work a new method SHSB (Self- Propagating High-Temperature Synthesis in Bath) has been used to produce of five new composites i.e.Ni3Al / TiC, Ni3Al / WC, Ni3Al / Zr, Ni3Al / NbC and Ni3Al /Ta...
Cast in situ composites of Ni3Al / MeC type
Composite in situ Intermetallic phase SHSB Process Exothermic reaction Carbides of TiC WC ZrC NbC TaC
2011/3/30
In this work a new method SHSB (Self- Propagating High-Temperature Synthesis in Bath) has been used to produce of five new composites i.e.Ni3Al / TiC, Ni3Al / WC, Ni3Al / Zr, Ni3Al / NbC and Ni3Al /Ta...
单晶Ni3Al裂纹扩展的TEM原位观察
Ni3Al 单晶 透射电镜 原位拉伸
2007/12/27
利用透射电镜(TEM)原位拉伸在室温下对(110)〖110〗取向Ni3Al合金单晶中裂纹的萌生与扩展进行了研究.结果表明:裂纹沿之字形路径扩展且裂纹的总体扩展路径与拉伸轴平行.迹线分析表明,首先激活的是(111)和(111)两个主滑移面上的滑移系;其后在Schmid因子为零的两个滑移面上的滑移系激活.为了解释所观察到的现象而建立了一个位错塞积模型.
热处理对NiCrAl/Ni3Al微叠层材料力学性能影响
电子束物理气相沉积 微叠层复合材料 力学性能
2013/10/9
利用电子束物理气相沉积技术(EB-PVD)制备NiCrAl/Ni3Al微叠层复合材料,对其在制备态和时效态不同温度下的力学性能进行试验,考察不同时效温度对材料拉伸性能的影响。结果表明,制备态样品沿柱状晶晶界发生脆性断裂,而热处理态样品的断口具有典型的韧性断裂特征。力学性能测试结果表明,经过适当的热处理后,微层材料室温和高温力学性能与制备态时相比,有明显的改善。经740℃/32h热处理后,材料性能明...
Ni3Al基合金IC6的防护涂层研究
IC6合金 MCrAlX包覆涂层 力学性能 抗氧化性能 抗腐蚀性能
2013/10/12
采用离子电弧镀的方法在Ni3Al基合金IC6上制备了NiCrAlY、NiCoCrAlY和NiCoCrAlYHf三种不同成分的MCrAlX包覆涂层,观察了涂层的微观组织,测试了带涂层试样的拉伸和高温持久等主要力学性能以及抗氧化和抗腐蚀性能.实验结果表明:涂层与合金基体的结合良好,各涂层均由γ',γ,β和α-Cr组成.扩散处理后,基体材料与涂层发生了元素的互扩散.NiCrAlY、NiCoCrAlY和N...