搜索结果: 1-8 共查到“复合材料 Ni3Al”相关记录8条 . 查询时间(0.037 秒)
Effect of gas corrosion on the character of phase boundaries in Ni3Al / WC composite
Composite in situ Phase Ni3A SHSB Process Carbide of WC Gas corrosion
2011/3/30
In view of quite specific physico-chemical and performance properties, the composite based on an intermetallic Ni3Al compound reinforced with tungsten carbides (WC) was selected for investigations. Th...
Effect of gas corrosion on the character of phase boundaries in Ni3Al / WC composite
Composite in situ Phase Ni3A SHSB Process Carbide of WC Gas corrosion
2011/3/30
In view of quite specific physico-chemical and performance properties, the composite based on an intermetallic Ni3Al compound reinforced with tungsten carbides (WC) was selected for investigations. Th...
Cr3C2/Ni3Al复合材料的高温稳定性
Ni3Al Cr3C2 复合材料 高温稳定性
2007/11/9
文章摘要:
通过对Cr3C2/Ni3Al复合材料在1000℃进行长期时效和氧化实验, 分别考察了该材料的高温相稳定性和化学稳定性. 结果表明, 经1000℃长期时效后, Cr3C2/Ni3Al复合材料中的Cr3C2强化相保持稳定,而基体中则析出一定量的γ相, 该相的析出强化了Ni3Al基体, 从而使得复合材料的硬度得到进一步提高. Cr3C2/Ni3Al复合材料具有优良的高温抗...
Ni3Al基复合材料的组织与性能
复合材料 Ni3Al基合金
2007/11/9
文章摘要:
通过机械法将NiAl粉、Ni粉WC粉混合后烧结, 堆焊制备成Ni3Al+WC复合材料. 研究结果表明, 该复合材料在堆焊过程中, 可促使大部分WC不溶入熔池而直接以颗粒状分布于Ni3Al基体上, 在WC的抗磨特性和基体的抗汽蚀性能联合作用下, 使该复合材料具有高的硬度及较好的抗汽蚀和抗水砂磨损的性能.
TiCx/Ni3Al复合材料相界面显微结构及界面纳米硬度与弹性模量分布
显微结构 纳米硬度 弹性模量
2007/11/9
文章摘要:
采用SEM,EDS等对融渗工艺制备的C/Ti比x分别为0.6、0.7、0.8和0.9的四种不同TiCx/Ni3Al复合材料进行了研究,证实Ti元素向金属相存在较强的扩散,而Ni和Al元素几乎没有向陶瓷相中扩散,扩散的结果形成了两相界面之间直接的原子结合,增加了复合材料相界面结合的强度和韧性.利用纳米压痕技术研究了复合材料相界面附近的纳米硬度H和弹性模量E,二者在相界...
Ni3Al/Ni7Hf2共晶的微观组织特征
2007/7/28
期刊信息
篇名
Ni3Al/Ni7Hf2共晶的微观组织特征
语种
中文
撰写或编译
作者
马书伟,郑运荣
第一作者单位
刊物名称
中国有色金属学报
页面
1996,Vol.6,No.4,P.158
出版日期
1996年
月
日
文章标识(ISSN)
相关项目
Ni7Hf2增强自生复合材料
Cr3C2/Ni3Al复合材料的组织与耐磨性能
Cr3C2/Ni3Al复合材料 堆焊 磨粒磨损
2013/10/9
采用氩弧焊将Cr3C2-Al-Ni焊丝堆焊于碳钢表面制成Cr3C2/Ni3Al高温耐磨复合材料。利用电弧物理热与Ni,Al反应热在线生成复合材料,增强相尺寸由原料中150μm经溶解析出减小到平均10μm以下,组织均匀稳定。复合材料常温下耐磨粒磨损性能是传统高温耐磨合金Stellite12的2倍。分析认为,在硬度几乎相同情况下,增强相体积分数、增强相尺寸、Ni3Al形变硬化能力是决定复合材料在常温下...